Sans Revêtement
Sans Revêtement
| Matières Premières |
Composition chimique en % |
Densité g/cm3 lb/in3 |
Résistivité @ 20°C µΩ.cm Ω cmil/ft |
Charge de Rupture |
Monobrin mm awg |
Toron mm² awg |
Laminé 
Fils de tressage | |
|---|---|---|---|---|---|---|---|---|
| écroui daN/mm² psi |
recuit daN/mm² psi | |||||||
| Cuprofor© (RoHS) | P 0.08% Co 0.28 % Cu Reste |
8,93 .321 |
2,30 13.836 |
65 94,000 |
40 58,000 |
0,020-0,800 20 to 56 |
0,005-3,30 10 to 40 |
|
| Green6 TM (RoHS) | Cu 99% Mg 1% | 8,93 .323 |
2,155 13.836 |
65 94,000 |
40 58,000 |
0,030-0,800 20 to 48 |
0,005-13,24 6 to 40 |
|
| Copper Clad Aluminum (CCA) | Cu 15% of the total weight | 3,63 .100 |
2,676 16.096 |
20 29,000 |
14 20,000 |
0,050-2,450 10 to 44 |
0,20 - 21 4 to 24 |
|
| Copper Clad Steel 40% IACS | Cu thickness 10% of the wire radius | 8,13 .294 |
4,397 26.450 |
75,8 110,000 |
34,5 50,000 |
0,040-1,000 18 to 46 |
0,035-3,30 12 to 34 |
- |
| High Purity Silver | 99.9 to 99.99% | 10,49 .379 |
1,610 9.685 |
35 50,000 |
19 27,000 |
0,025-1,000 20 to 50 |
0,005-3,30 12 to 40 |
|
| 990 Silver | Ag 99 % Cu 1 % | 10,49 .379 |
2,100 12.633 |
44 64,000 |
22 32,000 |
0,030-0,800 20 to 48 |
0,005-3,30 12 to 40 |
|
| 500 Silver | Ag 50 % Cu 50% | 9,70 .350 |
2,170 13.054 |
100 145,000 |
85 123,000 |
0,030-0,800 20 to 48 |
- |
|
| Pure Nickel | Ni 99.2 % | 8,93 .323 |
9,50 57.149 |
87 126,000 |
45 65,000 |
0,025-0,800 20 to 56 |
0,005-3,30 12 to 40 |
|
All data given in these tables should be considered as typical or average. Variations in properties can occur.
(*) Dual plating